产品名称:ESD C 2800 B-75A
订购热线:18820179977(微信同号)
产品说明:ESD C 2800 B-75A Black
Thermoplastic Polyolefin Elastomer (TEO)
Electrically Conductive
ESD Protection
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCEEnglish SI Metric ASTM
TESTSpecific Gravity 1.01 1.01 D 792 Molding Shrinkage 1/8 in (3.2 mm) section 0.0150 - 0.0300 in/in 1.50 - 3.00 % D 955
MECHANICALTensile Strength Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) 1300 psi 9 MPa D 412 Tensile Elongation Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) 450.0 % 450.0 % D 412 Tensile Stress Die C 0.125 in, 20 in/min (3.2 mm, 500 mm/min) @ 100 % 600.0 psi 4.1 MPa D 412 Tear Strength, Die C 235.0 pli 41.2 N/mm D 624 Hardness Shore A, 10 s delay 75 75 D 2240
ELECTRICALVolume Resistivity < 1000 ohm.cm < 1000 ohm.cm D 257 Surface Resistivity < 1E5 ohm/sq < 1E5 ohm/sq D 257
ESD STM11.11PROPERTY NOTES Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
GENERAL PROCESSING FOR INJECTION MOLDINGEnglish SI Metric Injection Pressure 12000 - 18000 psi 83 - 124 MPa Melt Temperature 360 - 410 °F 182 - 210 °C Mold Temperature 60 - 150 °F 16 - 66 °C Drying 2 hrs @ 175 °F 2 hrs @ 79 °C Moisture Content 0.03 % 0.03 % Dew Point 0 °F -18 °C
PROCESSING NOTES23 Apr 2008 SAC
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.
Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.