产品名称:ESD C 203 (RTP公司)
订购热线:18820179977(微信同号)
产品说明:ESD C 203
Nylon 6/6 (PA)
Glass Fiber
ESD Protection
Electrically Conductive
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCEEnglish SI Metric ASTM
TESTPrimary Additive 20 % 20 % Specific Gravity 1.31 1.31 D 792 Molding Shrinkage 1/8 in (3.2 mm) section 0.0050 - 0.0070 in/in 0.50 - 0.70 % D 955
MECHANICALImpact Strength, Izod notched 1/8 in (3.2 mm) section 1.1 ft-lbs/in 59 J/m D 256 unnotched 1/8 in (3.2 mm) section 7.0 ft-lbs/in 374 J/m D 4812 Tensile Strength 12000 psi 83 MPa D 638 Tensile Elongation 1.5 - 3.5 % 1.5 - 3.5 % D 638 Tensile Modulus 0.90 x 10^6 psi 6206 MPa D 638 Flexural Strength 17500 psi 121 MPa D 790 Flexural Modulus 0.85 x 10^6 psi 5861 MPa D 790
ELECTRICALVolume Resistivity < 1E3 ohm.cm < 1E3 ohm.cm D 257 Surface Resistivity < 1E6 ohm/sq < 1E6 ohm/sq D 257
ESD STM11.11Surface Resistance < 1E5 ohm < 1E5 ohm ESD STM11.11 Static Decay MIL-PRF-81705D, 5kV to 50 V, 12% RH < 2.00 s < 2.00 s FTMS101C
4046.1PROPERTY NOTES Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
GENERAL PROCESSING FOR INJECTION MOLDINGEnglish SI Metric Injection Pressure 10000 - 18000 psi 69 - 124 MPa Melt Temperature 530 - 570 °F 277 - 299 °C Mold Temperature 150 - 225 °F 66 - 107 °C Drying 4 hrs @ 175 °F 4 hrs @ 79 °C Moisture Content 0.20 % 0.20 % Dew Point 0 °F -18 °C
PROCESSING NOTESDesiccant Type Dryer Required.
1 Mar 2005 LCR
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.
Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.