产品名称:ESD C 100
订购热线:18820179977(微信同号)
产品说明:ESD C 100
Polypropylene (PP)
ESD Protection
Electrically Conductive
Standard (Low) MFR
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCEEnglish SI Metric ASTM
TESTSpecific Gravity 1.01 1.01 D 792 Melt Flow Rate @ 230 °C, / 2.16 kg 2.00 - 6.00 g/10 mi 2.00 - 6.00 g/10 mi D 1238 Molding Shrinkage 1/8 in (3.2 mm) section 0.0100 - 0.0170 in/in 1.00 - 1.70 % D 955
MECHANICALImpact Strength, Izod notched 1/8 in (3.2 mm) section 10.0 ft-lbs/in 534 J/m D 256 unnotched 1/8 in (3.2 mm) section No Break No Break D 4812 Tensile Strength 3400 psi 23 MPa D 638 Tensile Elongation > 10.0 % > 10.0 % D 638 Tensile Modulus 0.20 x 10^6 psi 1379 MPa D 638 Flexural Strength 4800 psi 33 MPa D 790 Flexural Modulus 0.19 x 10^6 psi 1310 MPa D 790
ELECTRICALVolume Resistivity < 1E3 ohm.cm < 1E3 ohm.cm D 257 Surface Resistivity < 1E6 ohm/sq < 1E6 ohm/sq D 257
ESD STM11.11Surface Resistance < 1E5 ohm < 1E5 ohm ESD STM11.11 Static Decay MIL-PRF-81705D, 5kV to 50 V, 12% RH < 2.00 s < 2.00 s FTMS101C
4046.1
THERMALIgnition Resistance* Flammability** HB @ 1/16 in HB @ 1.5 mm D 635 PROPERTY NOTES Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.* This rating is not intended to reflect hazards of this or any other material under actual fire conditions. ** Values per RTP Company testing.
GENERAL PROCESSING FOR INJECTION MOLDINGEnglish SI Metric Injection Pressure 10000 - 15000 psi 69 - 103 MPa Melt Temperature 375 - 450 °F 191 - 232 °C Mold Temperature 90 - 150 °F 32 - 66 °C Drying 2 hrs @ 175 °F 2 hrs @ 79 °C
PROCESSING NOTES4 Jan 2016 esg
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is
complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.
Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein.
Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all
molded articles will have the same properties as those listed.上一个产品:ESD C 101下一个产品:ESD C 100